DIAGNOSIS OF DAMAGE OF METALSTRUCTURES UNDER THE INFLUENCE OFCORROSION IN THE REGION OF DJIJEL

N/A
N/A
Info
Télécharger
Protected

Academic year: 2021

Partager "DIAGNOSIS OF DAMAGE OF METALSTRUCTURES UNDER THE INFLUENCE OFCORROSION IN THE REGION OF DJIJEL"

Copied!
1
0
0

Chargement.... (Voir le texte intégral maintenant)

Texte intégral

(1)

7th African Conference on Non Destructive Testing ACNDT 2016 & the 5th International Conference on NDT and Materials Industry and Alloys (IC-WNDT-MI)

2016

DIAGNOSIS OF DAMAGE OF METAL

STRUCTURES UNDER THE INFLUENCE OF CORROSION IN THE REGION OF DJIJEL

Mohammed-Amin BOUMEHRAZ, Mekki MELLAS

Abstract : The region of Djijel is characterized by a Mediterranean climate, its winters are cold and rainy unlike its autumns. It is also famous for its dry summers with a temperature ranging between 20 °C and 35 °C in summer, and average relative humidity of the air is high and can reach about 70%. Several physical and chemical damages were observed on the metal structures implanted in the Djijel region, these changes have directly affected their sustainability, such as: corrosion of steel profiles or reinforced concrete frames, cracks or/and coating bursting under the effect of alkali-aggregate reactions or corrosion of steel. In this study, we show some pictures from damage caused by corrosion of metal structures, then we explain the main causes of corrosion of steel profiles or degradation of reinforced concrete, and finally we propose some solutions or recommendations to avoid or reduce this structural damage

Keywords : Durability, corrosion, metal structures, humidity

Centre de Recherche en Technologies Industrielles - CRTI - www.crti.dz

Powered by TCPDF (www.tcpdf.org)

Références

Télécharger maintenant ( PDF - 1 Page - 7.94 KB )

Documents relatifs

DIAGNOSIS OF DAMAGE OF METAL STRUCTURES UNDER THE INFLUENCE OF CORROSION IN THE REGION OF DJIJEL

Several physical and chemical damages were observed on the metal structures implanted in the Djijel region, these changes have directly affected their

DURABILITY OF CONCRETE UNDER THE INFLUENCE OF SULPHATES ATTACK IN THE REGION OF OUARGLA – ALGERIA

Our experimental work aims to study the degradation mechanism physicochemical concrete specimens in the real aggressive environment as the building blocks of pipes and

CHANGES IN THE METAL COORDINATION SPHERE OF AZURIN AND STELLACYANIN UNDER INFLUENCE OF pH, OXIDATION/REDUCTION AND METAL SUBSTITUTION

L’archive ouverte pluridisciplinaire HAL, est destinée au dépôt et à la diffusion de documents scientifiques de niveau recherche, publiés ou non, émanant des

Physical conditions in the gas phases of the giant H II region LMC-N 11

Overall, the results agree with our study for LMC data points, that is, bright [C II ] components have a molecular gas fraction near unity, the contribution of neutral atomic gas to

Role of metal oxide nanoparticles in histopathological changes observed in the lung of welders.

Since this analysis revealed the presence of NP in macrophages in the alveolar lumen and in areas of fi- brous tissue in welders, our physico-chemist partner chem- ically synthesized

The problem of diagnosis with respect to physical parameters for changes in structures

L’archive ouverte pluridisciplinaire HAL, est destinée au dépôt et à la diffusion de documents scientifiques de niveau recherche, publiés ou non, émanant des

Sustainability of groundwater exploitation in the Mediterianean region

Faced with this s itu ation, various countries ha ve adopted water policie s for the conservation of groundwater resources, often inspired by the international paradigm

Physical and Chemical Conditions in the Horsehead Photodissociation Region

By comparing the abundances of different species derived in the Horsehead with those de- rived in other environments, we have obtained chemical diagnostics that can be used to