The influence of antagonist standardization on wear

KREJCI, Ivo, ALBERT, P., LUTZ, F.

Abstract

For differences among materials to be easily detected, low variation in in vitro wear tests is desirable. The working hypothesis of this paper was that antagonists standardized for shape and size and according to materials would show mean values similar to those found in natural, non-standardized cusps, and that standardization would lead to a reduction in mean variation.

First, the shapes and sizes of palatal cusps of non-erupted human upper third molars were measured. The cusp cupola was best described by the formula y = 0.001 x2 and was symmetrical around the axis of rotation. Up to 200 microm of the y-axis, this parabola corresponded best to a ball radius of 0.6 mm. Based on this information, standardized antagonists were fabricated from both human enamel and steatite. Wear in the occlusal contact area and the wear of opposing conventional ceramic and fine hybrid composite, respectively, were quantified in a computerized chewing simulator. As a control, natural human enamel cusps were used. Standardization of enamel cusps did not reduce the variation of the resulting wear compared with that of non-standardized enamel [...]

KREJCI, Ivo, ALBERT, P., LUTZ, F. The influence of antagonist standardization on wear.

Journal of Dental Research , 1999, vol. 78, no. 2, p. 713-9

PMID : 10029471

Available at:

http://archive-ouverte.unige.ch/unige:84759

Disclaimer: layout of this document may differ from the published version.

1 / 1

(2)

at IHEID on November 21, 2011 For personal use only. No other uses without permission.

jdr.sagepub.com Downloaded from

(3)

at IHEID on November 21, 2011 For personal use only. No other uses without permission.

jdr.sagepub.com Downloaded from

(4)

at IHEID on November 21, 2011 For personal use only. No other uses without permission.

jdr.sagepub.com Downloaded from

(5)

at IHEID on November 21, 2011 For personal use only. No other uses without permission.

jdr.sagepub.com Downloaded from

(6)

at IHEID on November 21, 2011 For personal use only. No other uses without permission.

jdr.sagepub.com Downloaded from

(7)

at IHEID on November 21, 2011 For personal use only. No other uses without permission.

jdr.sagepub.com Downloaded from

(8)

at IHEID on November 21, 2011 For personal use only. No other uses without permission.

jdr.sagepub.com Downloaded from

Références

Télécharger maintenant ( PDF - 8 Page - 2.78 MB )

Documents relatifs

for the standardization state and status of this protocol

The encoding of an object type is simply how that object type is represented using the object type’s syntax.. Implicitly tied to the notion of an object type’s syntax and

(STD 1) for the standardization state and status of this protocol

Implementations that support the OTP extended responses described in this document MUST support the response with the "init-hex" and "init-word" type

(STD 1) for the standardization state and status of this protocol

If anonymous users have read and write access to the same area, the server can be used as a communication mechanism to anonymously exchange information.. Servers which

(STD 1) for the standardization state and status of this protocol

If the CEK from MSG1 is to be used to derive the KEK for MSG2 then MSG1 MUST contain an unprotectedAttrs Attribute of type id-aa-CEKReference with a single value using

(STD 1) for the standardization state and status of this protocol

Several objectives for this methods have been identified, like to enable an e-mail user to send and receive faxes from his/her e-mail interface, to allow some kind of

Quantification of the wear according to different approaches to a Hard Alloy « Z38CDV5-3 »

This approach has been used [12] to express the rate of wear in the form of volume of lost material per unit of energy dissipated (Figure.8) In the case of a unidirectional

In the later part of the paper, we develop quite natural applications of this theorem to Diophantine approximation and to discretization of linear maps

When Γ is weakly almost periodic, we deduce, from Lemma 12 together with Proposition 10, that the upper limits appearing in the uniform upper density D + (Γ) and the frequencies

µ0 since rejecting the null hypothesis in favor of the alternative would mean that the sample mean would have to be “low”

This is actually not a difficult thing to do (for a hypothesis test of means based on a normal or a t distribution).. By