Effect of brazing current on microstructure andmechanical behavior of WC-Co/AISI 1020 steelTIG brazed joint

N/A
N/A
Info
Télécharger
Protected

Academic year: 2021

Partager "Effect of brazing current on microstructure andmechanical behavior of WC-Co/AISI 1020 steelTIG brazed joint"

Copied!
1
0
0

Chargement.... (Voir le texte intégral maintenant)

Texte intégral

(1)

International Journal of Refractory Metals and Hard Materials

Volume 64, Issue 1, 2017, Pages 210-218

Effect of brazing current on microstructure and mechanical behavior of WC-Co/AISI 1020 steel

TIG brazed joint

B. Cheniti, D.Miroud, R.Badji, D.Allou, T.Csanádi, M.Fides, P. Hvizdoš

Abstract: In this work, the WC-Co carbide/1020 steel brazed joints which were prepared by Tungsten Inert Gas (TIG) process using different brazing currents have been studied. The peak temperature reached by increasing the brazing current caused remarkable inter-diffusion of Ni, Mn, Cu and Co elements between the braze and the base materials. The higher the brazing current was, the larger the diffusion extent of these elements became and the greater the WC rearrangement occured. As the diffusion rate of Ni towards the WC-Co was enhanced through increasing brazing current, a short range diffusion of Co element towards the braze was recorded. A Special Shear Test (SST) conducted at room temperature revealed the best bonding strength for the current of 80A.

Besides, hardness (HIT) and elastic modulus (EIT) values of the interfaces were situated between those of the braze and the base materials.

Keywords : WC-Co cemented carbide, TIG brazing, inter-diffusion, Interface, Nano-indentation

Centre de Recherche en Technologies Industrielles - CRTI - www.crti.dz

Powered by TCPDF (www.tcpdf.org)

Références

Télécharger maintenant ( PDF - 1 Page - 7.73 KB )

Documents relatifs

On the identification of the diffusion ageing mode of Ni/Cu assemblies

Since nickel grows in a nodular shape during the process (Fig. 1b), it cannot provide the required airtightness. Conversely, copper deposits in a continuous multilayer that is able

Comparative investigation of the Ni and the Feeffect on the structure andmechanical response ofa WC-W-Ni hardmetal obtained by infiltration

The chemical affinity between Fe and Ni, provided by the Fe powder and thebinder respectively, derived on the formation of the (Fe, Ni) solid solution and FeNi3

Microstructural and mechanical properties ofWC-Co/1020 steel joints obtained byoxyacetylene and TIG brazing process

The mechanical behavior is carried out through shear and micro-hardness test, they show that the presence of the new zone concentrated in WC particles beside the hard metal, makes

Microstructure and mechanical behavior ofdissimilar AISI 304L/WC-Co cermet rotaryfriction welds

The mechanical behavior investigated by nano-indentation measurements and nano-scratch tests revealed that, regardless the friction time effect and considering the 304 L ASS side,

Microstructure and mechanical behavior of dissimilar AISI 304L/WC-Co cermet rotary friction welds

The mechanical behavior investigated by nano-indentation measurements and nano-scratch tests revealed that, regardless the friction time effect and considering the

Keywords Abstract Investigation of WC decarburization effect on the microstructure and wear behavior of WC-Ni hardfacing under dry and alkaline wet conditions

The dissolution and decarburization phenomena of WC particles with the formation of W 2 C eutectic phase and their effect on the decohesion and pull out of the particles during

Effect of brazing current on microstructure and mechanical behavior of WC-Co/AISI 1020 steel TIG brazed joint

The peak temperature reached by increasing the brazing current caused remarkable inter-diffusion of Ni, Mn, Cu and Co elements between the braze and the base

Relation between the hardness and the PulsedEddy Current in the materials characterisation

It is used in detection of the defects, particularly in the determination of corrosions .The information contained in the receivedsignal gives the possibility to determine