Study of the effect of thin ALD oxide coatings on the stability of silver nanowire based transparent electrodes
Texte intégral
Documents relatifs
L’archive ouverte pluridisciplinaire HAL, est destinée au dépôt et à la diffusion de documents scientifiques de niveau recherche, publiés ou non, émanant des
In the case of transparent conducting films with applications in photovoltaic devices, the measurements of the electrical resistivity during many successive heating and
The optical analysis via transmittance and reflectance measurements revealed that the band gap energy Eg decreased from 3.29 eV to 1.5 eV in terms of Bi2S3 content. The
Therefore, if they are well prepared and electrodeposited they could lead to the fabrication of highly efficient devices.In this study, we investigate the effect of deposition time
This study reports the effect of deposition time on the electrochemical, structural, morphological and optical properties of Cu 2 O thin films electrodeposited on ITO
These measurements are performed using an atomic force microscope mode functioning contactThe obtained results on the preparation and characterization of transparent electrodes based
The obtained results on the preparation and characterization of transparent electrodes based on indium oxide ITO, shows that the ITO thin film has good transparency
was measured in situ during and after film deposition, as a function of film thickness, annealing temperature and annealing time, for pure Al films, films deposited in